Multi-adherent water-based antioxidant varnish with quick drying and direct application on steel, oxide, aluminum and galvanized, without the need for prior priming. Protects metals from oxidation, blackening, moisture and deterioration due to use and over time. Preserves the oxidized and aged appearance of the metal on which it is applied. Provides a excellent resistance to weathering and humidity up to 15 years . Finished with high adhesion, flexibility and resistance to bumps and scratches. Without smell. With film preservative against fungi and algae. Total guarantee against corrosion according to UNE EN ISO 12944 standard. Guaranteed by means of an external laboratory test. Oxirón Varnish Antioxidant Water offers the best performance of the market against corrosion, in its category (minimum thickness of film and with only one product). Triple action: neutralizes, repairs and protects.
Exterior and interior. Ideal for gates, benches, garden elements, doors.
- Nature Co-polymer acrylic
- Matte finish
- Color (UNE EN ISO 11664-4) Colorless
- Density (UNE EN ISO 2811-1) 1.03 - 1.05 kg / l
- Performance (UNE 48282) 10 - 12 m² / l
- Drying at 23ºC 60% RH (UNE 48301) 30 - 60 minutes
- Repainted at 23ºC 60% RH (UNE 48283) From4 hours
- Application Methods Brush, roller and gun
- Water Thinner
- Water Utensils Cleaning
- Recommended thickness (UNE EN ISO 2808) 70 - 80 μ
- Application Conditions, HR <80% +10 ºC - +30 ºC
- Solid Volume (UNE EN ISO 3233-3) 38 - 40%
- VOC (UNE EN ISO 11890-2) 2.004 / 42IIA (i) (140/140) Max. VOC 80 g / l
Variations of temperature, humidity, thickness, dyeing or type of support, etc., can cause changes in drying, performance or other properties.
Corrosion tests in artificial atmospheres. Salt spray test UNE EN ISO 9227: Test duration 240h: Blistering UNE EN ISO 4628-2: 0 (S0) / Corrosion UNE EN ISO 4682-3: Ri0
Superiority test on oxidized steel: corrosion tests in artificial atmospheres. Salt spray test UNE EN ISO 9227: Test duration 240h: Corrosion UNE EN ISO 4682-3: Ri0 (89μ dry)
Determination of the covering power UNE EN ISO 6504/3: 9,14 m2 / l (98% Covering power) Class 2
Reaction to Fire UNE EN 13501-1 + A1: B-s1, d0 / on metal substrate Emission VOC ISO 16000-6: A +
Resistance against seaweed UNEEN 15458:Growth 1
Resistance to fungi UNE EN 15457:Growth 1
Determination of resistance to liquids. Method using an absorbent medium according to UNE-EN ISO 2812-3: Without changes
Community Ecological Label for interior and exterior paints and varnishes (Ecolabel)
How to use
The surfaces to be painted must be degreased, dry and free of loose rust, scale and dirt.
SURFACES NOT PREPARED: Steel:
It can be applied directly without primer. If the surface presents rust, sand lightly to confer roughness to the substrate, eliminating the bad adhering oxide. In medium corrosion environments, the steel must be sanded to grade ST 3 of the UNE EN ISO 8501-1 standard. Under these conditions a minimum thickness of 100 microns (3 dry hands) will be necessary. Aluminum and galvanized steel: Sand down to shade and apply directly Oxiron Antioxidant Water Varnish. Other supports: Consult.
MAINTENANCE OF PAINTED SURFACES IN BAD CONDITION:
Eliminate rust and poorly adhered paint coatings with emery cloth or barbed brush.For the application of the finish, proceed as on unprepared surfaces.